hard ferrite magnet from China manufacturer - Ningbo Able Magnetic Co., Ltd.

Price:	10.0 USD
Payment Terms:	T/T,L/C,WU
Place of Origin:	Zhejiang, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Means of Transport: Ocean,Land,Air

Packing: packing as customer's reque...

Application: Motor Magnet

Type: Permanent

Brand Name: Able Magnet

Certificate: SGS, RoHS

Main Market: Worldwide

Production Capacity: 50,000,000pcs per month

Delivery Date: Within 30 days

Shape: Others

Composite: Ferrite Magnet

Name: ferrite magnet

Port of loading: Ningbo, Shanghai

Product name:ferrite magnets
Type:permanent
Composite:ferrite magnet
Shape:ring
Application:motor,speaker

Product name:ferrite magnets

Developed in the late 1950's Sintered Ferrite or Ceramic magnets are manufactured from a composite powder containing 80% Iron oxide and 20% Barium or Strontium oxide. This powder is die pressed into a component that is then sintered in a furnace at approximately 1200°C.

Ferrites suit a wide range of applications due to their low cost. They are readily available in blocks, rings and discs. Principal applications are DC motors, loudspeakers, reed switch operation, magnetic separator assemblies and general holding devices such as pot magnets. The unmagnetised blocks are machined using diamond cutting machines to match customers' exact specification.

Ferrite has an excellent resistance to demagnetisation and can be magnetised before or after assembly without danger of losing any performance. It can be used in operating temperatures ranging from -40°C to + 250°C. However it does have a poor temperature coefficient losing approximately 0.2% of remanence per degree C when heated above zero.

Sintered Ferrite will not corrode even in salt-water applications. It also has good chemical stability, with the only exceptions being concentrated acids such as hydro-chloric.

With mechanical properties similar to ceramics or porcelain, it means that only grinding techniques can be used to machine these products. Care is required during handling due to their brittle nature.

TYPICAL MAGNETIC AND PHYSICAL SPECIFICATIONS AT 20°C
MSS GRADE	DIN	Br		bHc		jHc		(BH) max		Magnatising Force (Minimum)		Max. working temp (°C)	Density (g/cc)	Rev Temp Coeff.of Br % °C
MSS GRADE	DIN	T	Gauss	kA/m	Oersted	kA/m	Oersted	kJ/m3	MGO	kA/m	Oersted	Max. working temp (°C)	Density (g/cc)	Rev Temp Coeff.of Br % °C
FER1	8/22	.220	2200	136	1700	220	2750	8	1.0	600	7500	250	4.8	-0.19
FER2	28/18	.400	4000	160	2000	185	2300	28	3.5	800	10000	250	5.0	-0.19
FER3	26/26	.370	3700	240	3000	260	3250	26	3.3	800	10000	250	4.9	-0.19